Product introduction
CORONATE 2604 and CORONATE 2610 are aromatic/aliphatic polyfunctional isocyanates. The drying performance of CORONATE 2604 and CORONATE 2610 is slower than CORONATE 2030 but much faster than CORONATE L. CORONATE 2604 and CORONATE 2610 have better weathering properties than CORONATE L and CORONATE 2030. CORONATE 2604 is known for its improved weathering properties and CORONATE 2610 is used to improve drying properties.
General parameters
|
CORONATE 2604 |
CORONATE 2610 |
Company A product |
Exterior |
light yellow liquid |
light yellow liquid |
light yellow liquid |
NCO content (wt%) |
10.6 |
10.6 |
10.5 |
Solid content (wt%) |
60 |
60 |
60 |
Viscosity at 25°C (cP) |
500 |
1200 |
(2200/23C) |
Free TDI (wt%) |
Max.0.2 |
Max.0.2 |
NA |
Hue (Gardener) |
Below 2 |
Below 2 |
NA |
solvent |
Butyl acetate |
Butyl acetate |
Butyl acetate |
dry condition
|
C-2604 |
C-2610 |
C-2030 |
C-L |
Product“A” |
Dry to touch (min) |
7 |
6 |
3 |
35 |
8 |
Completely dry (min) |
53 |
50 |
25 |
>100 |
52 |
Test Conditions
Polyol |
Acrydic A-801, DIC product |
NCO/OH |
1/1 (mol) |
Solid content in paint |
50wt% |
solvent |
Butyl acetate/xylene = 1/1 (wt ratio) |
Film thickness |
25μ |
Coating Test
|
hardness |
bond strength |
Elasticity (mm) |
Impact strength |
Bending performance |
C-2604 |
H |
20/100 |
1.2 |
Max. 5cm |
Passed |
C-2610 |
H |
30/100 |
1.2 |
Max. 5cm |
Passed |
C2030 |
H |
0/100 |
1.0 |
Max. 5cm |
Passed |
C-L |
F |
100/100 |
1.0 |
20cm |
Passed |
Product“A” |
H |
30/100 |
1.0 |
Max. 5cm |
Passed |
Hardness: Pencil scratch test
Adhesive Strength: De-lamination Test in “cross cut method”
Elasticity: Ericksen
Impact Strength: Dupont method 1/2 inch x 1,000g
Bending performance: 4mmφ
Test Conditions
Polyol |
Acrydic A-801, DIC product |
NCO/OH |
1/1 (mol) |
Solid content in paint |
40wt% |
PWC |
40wt% (TiO2, manufactured by Ishihara Sangyo Co., Ltd.) |
solvent |
Butyl acetate/Xylene = 1/1 (wt ratio) |
Film thickness |
30 μ 20C, 65%RH, for 1 week. |
Weathering properties (QUV)
|
Time |
|||
Product |
|
0hr. |
240hrs. |
400hrs. |
CORONATE 2604 |
Luster(%) ΔYI ΔE |
86 - - |
56 (66%) 7.1 4.0 |
24 (28%) 7.7 4.2 |
CORONATE 2610 |
Luster(%) ΔYI ΔE |
87 - - |
54 (62%) 8.7 4.9 |
20 (23%) 9.0 4.9 |
C-2030 |
Luster(%) ΔYI ΔE |
86 - - |
30 (35%) 20.3 13.7 |
- - - |
C-L |
Luster(%) ΔYI ΔE |
87 - - |
12 (14%) 27.2 19.4 |
- - - |
Product “A” |
Luster(%) ΔYI ΔE |
76 - - |
47 (62%) 9.1 5.1 |
24 (32%) 10.1 5.5 |
YI; Yellow Index