Cashew Nut Shell Oil Bio-based Modified Polyol FX-9014 - 广州昊毅新材料科技股份有限公司

Cashew Nut Shell Oil Bio-based Modified Polyol

Cashew Nut Shell Oil Bio-based Modified Polyol FX-9014

                                                    

 

Cashew Nut Shell Oil Bio-based Modified Polyol FX-9014

   Guangzhou Polycarbon provides a range of renewable polyol products for polyurethane formulations.

Cashew nut shell oil products exhibit excellent water resistance, low moisture sensitivity, and balanced mechanical strength.

Cashew nut shell oil polyols provide excellent chemical resistance, especially alkali resistance.

Key markets include coatings, adhesives, potting, foams and composites.

Hydroxyl value (mg KOH/g)

256

Viscosity (cps@25℃)

1200

functionality

4.3

Color (Ghanaian Law)

5

Remark

High strength, better color stability

 

Mechanical behavior

formula

FX-9014/PMDI

=10061.8

Tensile strength (MPa)

27.2

Shore D hardness

76

Lap Shear Strength,(MPa)

13.710 on AI

Elongation at break (%)

43

Tg(°C)

37

curing conditions

70/4hr+120/2.5hr

 

 Curing speed  

formula

FX-9011/PMDI

=100/56

Hard dry (hours) at 25°C

2.9

Hard dry (hours) at 5°C

8.2

Hard dry (hours) at 0°C

-

 

  Hydrolytic stability

Polyol samples, cured with polymeric MDI

(NCO index=100)

FX-9014

Lap Shear Strength (MPa), Control Sample

13.2

After 80°C/7 days water immersion test

Lap Shear Strength (MPa)

5.7

Lap shear strength drop (%)

56.6

 

 