Chemical name: Chlorinated polypropylene resin
General Features:
Chlorine content |
24%-26% |
Viscosity |
10-100mPa.S (25℃, dissolve into 20% solid content solution with toluene) |
solution |
transparent |
softening temperature |
Around 70℃ |
dry film state |
Colorless, transparent, soft, thermoplastic resin |
solid state |
yellowish lump |
Solubility:
Soluble solvents: aromatic hydrocarbons - toluene, xylene, etc.
Aliphatic hydrocarbons—cyclohexane, methylcyclohexane, ethylcyclohexane, etc.
Ketones---MEK, MIBK, etc.
Esters---ethyl acetate, butyl acetate, etc.
Slightly soluble solvents: methanol, ethanol, butanol (alcohols); hexane, heptane (alkanes).
(mPa.s@25℃/20% solid content)
solvent |
Viscosity |
Dissolution |
Ethyl acetate (EA) |
40 |
Not clear |
Methylcyclohexane (MCH) |
60 |
Not clear |
Methyl Ethyl Ketone (MEK) |
30 |
Not clear |
EA/MCH=1/1 |
45 |
fully soluble |
EA/MCH=4/1 |
40 |
fully soluble |
MCH/MEK=1/1 |
40 |
fully soluble |
MCH/MEK=1/4 |
35 |
fully soluble |
EA/MCH/IPA=5/4/1 |
45 |
fully soluble |
EA/MCH/IPA=9/9/2 |
40 |
fully soluble |
EA/MCH/MEK=4/3/3 |
40 |
fully soluble |
EA/MCH/MEK=5/2/3 |
40 |
fully soluble |
MCH/MEK/IPA=4/5/1 |
40 |
fully soluble |
MCH/MEK/IPA=9/9/2 |
40 |
fully soluble |
Xylene |
45 |
fully soluble |
Features:
825S is a high-performance chlorinated polypropylene resin, which is made of isotactic high-grade PP chlorinated and then grafted with functional groups. After being melted into a liquid state, it has excellent adhesion to various types of plastic materials, and is compatible with large Some common solvent-based resins have good affinity and are widely used in one-component advanced coating systems.
After the 825S resin is dissolved into a liquid, it has good resistance to low temperature freezing, and the solution does not freeze at (-5°C to 0°C).
主要用途 :
1. Plastic composite binder.
2. Gravure plastic composite ink binder.
3. PP, PET, ABS, PVC use material binder.
4. Heat resistant ink binder.
5. Anti-corrosion coating binder.