INV ES-1406B Special curing agent for optical coatings - 广州昊毅新材料科技股份有限公司

Optical crosslinking agent

INV ES-1406B Special curing agent for optical coatings

                                         

 

Product introduction
    INV ES-1406B is a blocked cycloaliphatic polyisocyanate supplied as a 60% solids solution in butyl acetate.

 

  Typical data

nature

Numerical value

unit

testing method

solid content

60 ±2

wt%

DIN EN ISO 3251 (75min65)

Viscosity@23℃

500±100

mPa·s

DIN EN ISO 3219

free NCO

< 0.3

wt%

DIN EN ISO 11 909 ASTM D 2572

NCO equivalent (solution)

600

g/Eq

-

Decapsulation temperature

120

-

Chromatic Number (Gardner)

< 2

-

DIN ISO 4630 ASTM D 1544

Flash point (closed cup)

32

DIN EN ISO 2719

Density@23℃

1.02±0.02

g/cm3

DIN 51 757

 

  Properties and applications 
      INV ES-1406B can be used to crosslink suitable hydroxyl resins such as polyester, acrylic or alkyd resins.
INV ES-1406B can be formulated for thermosetting polyurethane coatings with curing temperature higher than 120℃.

Storage and Packaging
INV ES-1406B should be stored in a dry indoor place at a storage temperature of 5°C to 30°C, avoiding direct sunlight. It can be stored in an unopened container for at least one year without changing the quality listed above.
The INV ES-1406B is packaged in 475lb (15.46kg) or 55lb (24.95kg).

Safe operation
For product safety and handling instructions, please consult the Material Safety Statement (MSDS) for this product.