Other curing agents

Japan Mitsui Chemicals Takenate D110N D-110N

Product introduction
Takenate D-110N is a curing agent for aliphatic polyisocyanates synthesized from xylylene diisocyanate (XDI) dissolved in ethyl acetate.

Features
Good weather resistance, anti-yellowing and adhesion;
Curability is better than TDI aromatic polyisocyanates;
It is used in conjunction with resins containing hydroxyl groups such as polyols and castor oil, and is mainly used in coatings, adhesives and sealing materials.
state property

Exterior	light yellow transparent liquid
Chroma G	1 Max.
Solid content%	75.0±1.0
Viscosity 25°C, mPa s	500±400
NCO content%	11.5±0.5
Free XDI Monomer %	0.5 Max.

Coating Properties*

main agent	TTakelac U-27 (polyester polyol)
Mixing ratio, NCO/OH molar ratio	1.0
Shiatsu drying, h	2.4
activity, h	8
adhesion	100/100
Erickson value, mm	8
Bending resistance, mm	2
impact resistance
DuPont method, inch x g x cm	1/2 x 1000 x 50
pencil hardness	H

*The data provided here is measured only during normal use and does not represent the specifications of this product.

Scope of application
Can be used as woodworking, furniture, interior, vehicle, paper, plastic coating, outdoor protective coating components, adhesives, sealants, ink adhesives, etc.

Precautions
Please refer to MSDS for health and safety related information of this product.