Japan UBE Hybrid Polycarbonate Glycol PH Series PH-100 PH-200… - 广州昊毅新材料科技股份有限公司

Polycarbonate diol PCDL

Japan UBE Hybrid Polycarbonate Glycol PH Series PH-100 PH-200…

                                                         

 

  Product introduction  
       "ETERNACOLL® PH" is the trade name of a mixed polycarbonate diol developed by Ube Industries, which uses 1,5-pentanediol and 1,6-hexanediol as polymerized monomers.

 Specifications  

Product indicators

PH 50

PH 100

PH 200

PH 300

apparent

viscous liquid

average molecular weight

Ca. 500

Ca. 1000

Ca. 2000

Ca. 3000

Base number (KOH mg/g)

224 ± 20

110 ± 10

56 ± 5

37 ± 3

Acid value (KOH mg/g)

0.1

<0.1

<0.1

<0.1

Chroma (APHA)

<100

<100

<100

<100

Moisture content (wt%)

<0.1

<0.1

<0.1

<0.1

Viscosity

65-120

400-630

2200-2800

6500-9800

 

Polyurethane synthesis conditions

Molar ratio ETERNACOLL® UH: 1,4-BD: MDI=1:2:3
Polymerization temperature 80°C, 5hrs in DMF
Film Casting 70°C, 1hr ¦ 120°C, 2hrs

 

 

 Test Results

Product indicators

Detection method

unit

PH-100

PH-200

proportion

ISO 1183

g/cm3

1.22

1.20

Hardness (ShoreA)

 

 

89

86

Elongation factor 100 %1

ISO 527

MPa

34

9

Elongation factor 200 %1

ISO 527

MPa

66

18

Elongation factor 300 %1

ISO 527

MPa

--

33

Tensile Strength 1

ISO 527

MPa

75

53

Elongation at break1

ISO 527

%

222

399

Film tear strength

ISO 34

MPa

154

85

Abrasion resistance 2

 

mg

11

8

glass transition temperature 3

DSC

ºC

-12

-28

 

1. The rate is 300 mm/min.
2. Taber, H-22 wheel, 1kg load, 1000 cycles
3. Heating rate: 10 ºC/min

 

 Product Features

product properties

Detection method

unit

PH-100

PH-200

paint 1

 

 

 

 

Viscosity

 

cps

87

31

drying time 2

ASTM D5895-03

hours

<2

<2

Paint 3

 

 

 

 

Hardness (Persoz)

ISO 1522

 

46

59

Gloss

ISO 2813

%

99

97

chemical resistance

ISO 4211

 

4

4

Heat resistance: 50 days in an oven at 120°C

1. Solids % w/w = 38, prepolymer NCO/OH ratio = 1.5, prepared by acetone method
2. Completely dry (23℃, 50% RH)
3. After 7 days at a temperature of 23°C and a relative humidity of 50%, measured on a stainless steel plate (ISO 1514)

Water resistance: submerged in water at 80°C for 60 days
Oil resistance: immersion in BP CS 150 at 100°C for 30 days
Weather resistance: 200 hours exposure to 340nm wavelength beam through weathering instrument
radiation dose 35 Wm2/nm
Black mark temperature 65℃±3℃
             Relative humidity
Dry for 102 minutes, then spray with water for 18 minutes
(rain test)