Cashew Nut Shell Oil Bio-based Modified Polyol FX-9011 - 广州昊毅新材料科技股份有限公司

Cashew Nut Shell Oil Bio-based Modified Polyol

Cashew Nut Shell Oil Bio-based Modified Polyol FX-9011

                                                        

 

 Cashew Nut Shell Oil Bio-based Modified Polyol FX-9011

     

Guangzhou Polycarbon provides a series of renewable polyol products for polyurethane formulations.

Cashew nut shell oil products exhibit excellent water resistance, low moisture sensitivity, and balanced mechanical strength.

Cashew nut shell oil polyols provide excellent chemical resistance, especially alkali resistance.

Key markets include coatings, adhesives, potting, foams and composites.

 

Hydroxyl value (mg KOH/g)

224

Viscosity (cps@25℃)

1710

functionality

3.1

Color (Ghanaian Law)

5

Remark

High hardness and flexibility

 

  Mechanical behavior

formula

FX-9011/PMDI

=10056

Tensile strength (MPa)

30

Shore D hardness

78

Lap Shear Strength,(MPa)

11.5

Elongation at break (%)

70

Tg(°C)

46

curing conditions

25/4day+60/24hr

 

 Curing speed

formula

FX-9011/PMDI

=100/56

Hard dry (hours) at 25°C

2.7

Hard dry (hours) at 5°C

8.9

Hard dry (hours) at 0°C

-

 

 Hydrolytic stability

Polyol samples, cured with polymeric MDI

(NCO index=100)

FX-9011

Lap Shear Strength (MPa), Control Sample

9.9

After 80°C/7 days water immersion test

Lap Shear Strength (MPa)

6.9

Lap shear strength drop (%)

29.7