Chemical name:Chlorinated polypropylene resin
General Features:
Chlorine content |
40%-42% |
Viscosity |
1000-5000mPa.S (25℃, dissolve into 40% solid content solution with ethyl ester or butyl ester) 20-100mPa.S (25℃, dissolve into 20% solid content solution with toluene) |
solution |
transparent |
softening temperature |
Around 70℃ |
dry film state |
Colorless, transparent, soft, thermoplastic resin |
solid state |
yellowish lump |
Solubility :
Soluble Solvents: Aromatic hydrocarbons—toluene, xylene, etc.
Aliphatic hydrocarbons—cyclohexane, methylcyclohexane, ethylcyclohexane, etc.
Ketones---MEK, MIBK, etc.
Esters---ethyl acetate, butyl acetate, etc.
Slightly soluble solvents: methanol, ethanol, butanol (alcohols); hexane, heptane (alkanes).
(mPa.s@25/20% solid content)
solvent |
Viscosity |
Dissolution |
Ethyl acetate (EA) |
40 |
fully soluble |
Methylcyclohexane (MCH) |
60 |
fully soluble |
Methyl Ethyl Ketone (MEK) |
30 |
fully soluble |
EA/MCH=1/1 |
45 |
fully soluble |
EA/MCH=4/1 |
40 |
fully soluble |
MCH/MEK=1/1 |
40 |
fully soluble |
MCH/MEK=1/4 |
35 |
fully soluble |
EA/MCH/IPA=5/4/1 |
45 |
fully soluble |
EA/MCH/MEK=4/3/3 |
40 |
fully soluble |
EA/MCH/MEK=5/2/3 |
40 |
fully soluble |
MCH/MEK/IPA=4/5/1 |
40 |
fully soluble |
MCH/MEK/IPA=9/9/2 |
40 |
fully soluble |
Toluene |
45 |
fully soluble |
Other features:
841S has excellent frost resistance, and the solution does not freeze in the range of -5℃-0℃. 841S can be completely dissolved with ethyl ester, and the viscosity after dissolution is low, which is suitable for the ink and coating industry with relevant requirements.
The main purpose:
1. Plastic composite binder.
2. Gravure plastic composite ink binder.
3. PP, PET, ABS, PVC use material binder.
4. Heat resistant ink binder.
5. Anti-corrosion coating binder.
Package :
20Kg/box (carton)