Adiko Photothermal Curing Material Series UV Thermal Curing Resin
UV topcoat
| Product number | Purpose | Features | Viscosity/cP | Recommended substrate | Recommended processing conditions |
| KRX-3200 | General Surface Coating | Standard | 50-200 | PET/glass/plastic | Coating: Offset/Slot/Stick Film thickness: 3-10μm UV hardening: 500-1000mJ/cm² |
| KRX-3201 | Tube coating | heat seal bonding | 200-350 | PE (corona treated) PET/glass/plastic |
Coating: Offset/Slot/Stick Film thickness: 3-5μm UV hardening: 100-500mJ/cm² |
| KRX-3202 | smoothness | 200-350 | |||
| KRX-3203 | General Surface Coating | softness | 100-300 | PET/plastic | Coating: Offset/Slot/Stick Film thickness: 3-10μm UV hardening: 500-1000mJ/cm² |
| KRX-3204 | Tube coating | heat seal bonding | 300-500 | PE (corona treated) PET/glass/plastic |
Coating: Offset/Slot/Stick Film thickness: 3-5μm UV hardening: 100-500mJ/cm² |
| KRX-3205 | General Surface Coating | High transparency | 200-500 | PET/glass/plastic | Coating: Offset/Slot/Stick Film thickness: 5-10μm UV hardening: 50-1000mJ/cm² |
| KRX-3206 | Low viscosity | 40-60 | PET/PC/plastic |
Delayed curing adhesive
| Product number | Features | hardening type | Recommended substrate | Recommended hardening conditions | Resin properties | |
| Exterior | Viscosity/cP | |||||
| KRX-2200 | delayed hardening | UV+heat | PET Glass various plastics |
Film thickness: 5-100μm Hardening: UV300-3000mJ/cm² 120℃ 1hr |
Light yellow transparent liquid | 2500-4000 |
| KRX-2201 | delayed hardening Thixotropy |
cloudy liquid | 5000-20000 Thixotropic ratio 0.5-4 |
|||
| KRX-2202 | super delayed hardening | Film thickness: 5-50μm Hardening: UV300-3000mJ/cm² 120℃ 1hr |
Light yellow transparent liquid | 1000-5000 | ||
| KRX-2204 | delayed hardening high transparency |
1500-3000 | ||||
| KRX-2210 | low viscosity delayed hardening |
40-60 | ||||
| KRX-2211 | high viscosity delayed hardening |
Film thickness: 10-100μm Hardening: UV300-3000mJ/cm² 120℃ 1hr |
10000-14000 | |||
conventional adhesive
| Product number | Features | hardening type | Recommended substrate | Recommended hardening conditions | Resin properties | |
| Appearance | Viscosity/cP | |||||
| KRX-3200 | low viscosity | UV | PET various plastics |
Film thickness 2-50μm Hardening: UV300-3000mJ/cm² |
Light yellow transparent liquid | 50-200 |
| KRX-3203 | softness | 100-300 | ||||
| KRX-3205 | High transparency | PET/glass various plastics |
200-500 | |||
| KRX-3206 | low viscosity | PET PC various plastics |
40-60 | |||
| KRX-3089 | strong adhesion High transparency |
Film film 20-50 μm Curing: 60-120 ° C for 3 minutes UV500-3000mJ / cm² |
9000-11000 | |||
| KRX-3090 | 4000-6000 | |||||
| KRX-3219 | low penetration | UV+heat | PET Glass various plastics |
Film thickness 5-50μm Hardening: UV300-3000mJ/cm² 120℃ 1hr |
1000-2500 | |
| KRX-3217 | low viscosity | 50-200 | ||||
| KRX-3300 | Medium-high viscosity | 4000-8000 | ||||
Optical UV Resin
| Product name | KRX-3209 | KRX-3210 | |||
| Features | High Refractive Index | Low Refractive Index | |||
| Resin properties | Appearance | Light yellow transparent liquid | Light yellow transparent liquid | ||
| Viscosity/cP | 2000-3000 | 2000-3000 | |||
| Recommended hardening conditions | Substrate: MS, PS, PMMA, PCP, PET Coating method: gravure, slit, rod Solid content film thickness: 10-100μm UV hardening: 1000-2000mJ/cm² |
||||
| Hardened physical properties | Refractive index | 1.59 | 1.52 | ||
| Glass transition temperature | 43℃ | 73℃ | |||
| Elasticity | 25℃ | 1860MPa | 1910MPa | ||
| 50℃ | 45MPa | 660MPa | |||
| 100℃ | 20MPa | 75MPa | |||
| Pencil Hardness | F | F | |||
| Hardening shrinkage | 7% | 7% | |||